410S Neoksidebla ŝtalo Bobeno
Priskribo
Specifoj:
1.Normo: ASTM A240, JIS G4304, EN10088
2. Grado: 200serio & 300serio & 400serio
3. Dikeco: 0.03mm - 6.0mm
4. Larĝo: 8mm-600mm
5. Longo: kiel la peto de klientoj
6. Surfaco: 2D, 2B, BA, Spegulo finita, N04, Harlinio, Matt finpoluro, 6K, 8K
7.Teknologio: malvarma tirita / malvarma ruliĝita / varma rulita
Materialoj:
| Tajpu | Grado | Grado | Kemia Komponanto % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Alia | |||
| Aŭstenita | 201 | SUS201 | ≤0,15 | 16.00-18.00 | 3.50-5.50 | 5.50–7.50 | ≤0,060 | ≤0,030 | - | ≤1.00 | - | ≤0,25 | - |
| 202 | SUS202 | ≤0,15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0,060 | ≤0,030 | ≤1.00 | - | ≤0,25 | － | ||
| 301 | 1.4310 | ≤0,15 | 16.00-18.00 | 6.00-8.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | ≤0,10 | - | |
| 304 | 1.4301 | ≤0,07 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 304L | 1.4307 | ≤0,030 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 304H | 1.4948 | 0.04-0.10 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 309 | 1.4828 | ≤0,20 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 309S | * | ≤0,08 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 310 | 1.4842 | ≤0,25 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 310S | * | ≤0,08 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 314 | 1.4841 | ≤0,25 | 23.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1.4401 | ≤0,08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316L | 1.4404 | ≤0,030 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316Ti | 1.4571 | ≤0,08 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | 0.1 | Ti5(C+N)~0.70 | |
| 317 | * | ≤0,08 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 317L | 1.4438 | ≤0,03 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 321 | 1.4541 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Ti5(C+N)~0.70 | |
| 321H | * | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Ti5(C+N)~0.70 | |
| 347 | 1.4550 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Nb≥10*C% -1.10 | |
| 347H | 1.494 | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Nb≥10*C% -1.10 | |
| Dupleksa | 2205 | S32205 | ≤0,03 | 22.0-23.0 | 4,5-6,5 | ≤2.00 | ≤0,030 | ≤0,020 | 3.0-3.5 | ≤1.00 | - | 0.14-0.20 | |
| 2507 | S32750 | ≤0,03 | 24.0-26.0 | 6.0-8.0 | ≤1,20 | ≤0,035 | ≤0,020 | 3.0-5.0 | ≤0,80 | 0.5 | 0.24-0.32 | ||
| Ferito | 409 | S40900 | ≤0,03 | 10.50-11.70 | 0.5 | ≤1.00 | ≤0,040 | ≤0,020 | - | ≤1.00 | - | ≤0,030 | Ti6(C+N)~0,50 Nb:0,17 |
| 430 | 1Cr17 | ≤0,12 | 16.00-18.00 | - | ≤1.0 | ≤0,040 | ≤0,030 | - | ≤1.0 | - | - | - | |
| 444 | S44400 | ≤0,025 | 17.50-19.50 | 1 | ≤1.00 | ≤0,040 | ≤0,030 | 1,75-2,5 | ≤1.00 | - | 0,035 | Ti+Nb:0.2+4(C+N)~0.80 | |
| Martensito | 410 | 1Cr13 | 0.08-0.15 | 11.50-13.50 | 0,75 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - |
| 410S | * | ≤0,080 | 11.50-13.50 | 0.6 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 420 | 2Cr13 | ≥0,15 | 12.00-14.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 420J2 | 3Cr13 | 0,26-0,35 | 12.00-14.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0,07 | 15.00-17.50 | 3.00-5.00 | ≤1.00 | ≤0,035 | ≤0,030 | - | ≤1.00 | 3.00-5.00 | - | Nb 0,15-0,45 |
| 631 | 17-7PH | ≤0,09 | 16.00-18.00 | 6.50-7.50 | ≤1.00 | ≤0,035 | ≤0,030 | - | ≤1.00 | ≤0,50 | - | Al 0,75-1,50 | |
| 632 | 15-5PH | ≤0,09 | 14.00-16.00 | 3.50-5.50 | ≤1.00 | ≤0,040 | ≤0,030 | 2.00-3.00 | ≤1.00 | 2,5-4,5 | - | Al 0,75-1,50 | |
Bazaj informoj
410s Neoksidebla Ŝtala Bobeno, kun bona koroda rezisto kaj maŝinebleco, ĝi estas ĝeneraluzebla ŝtalo kaj tranĉila ŝtalo.410S estas speco de ŝtalo, kiu povas plibonigi la korodan reziston kaj formablecon de 410-ŝtalo. 410S estas alta fortika ŝtalo, kiu povas plu plibonigi la korodan reziston de 410-ŝtalo.Ĝi estas uzata por turbinklingoj kaj alttemperaturaj partoj.
• Specifoj: AISI 410s, ASTM 410s
• Finoj: Ba surfaco, 2b surfaco, No.1 (blanka haŭto), 2D surfaco, No.4 (frostita), HL (drato desegno), 8K surfaco havas bonegan surfacan kvaliton
•Muelejaj toleremoj pri dikeco kaj ebeneco validas.Voku JM Steel se vi bezonas specifajn grandecojn aŭ grendirekton.
410S Karakteriza maŝinanta teknologio
1D -- La surfaco havas malkontinuan grajnecan formon, ankaŭ konatan kiel nebulsurfaco.
Pretiga teknologio: varma laminado + kalcia pafo peening peklado + malvarma rulado + kalma peklado.
2D - Iomete arĝenteca blanka koloro.
Pretiga teknologio: varma laminado + kalcia pafo peening peklado + malvarma rulado + kalma peklado.
2B -- Arĝenta blanka kun pli bona brilo kaj plateco ol 2D surfaco.
Pretiga teknologio: varmega ruliĝado + kalcia pafo peening peklado + malvarma ruliĝado + kalma peklado + estingi kaj hardi ruliĝadon.
Ba - Bonega surfaca brilo, alta reflektiveco, kiel spegula surfaco.
Pretiga teknologio: varma laminado + kalcia pafo peening pikado + malvarma rulado + kalma peklado + surfaca polurado + estingi kaj hardi ruliĝadon.
No.3 -- Bona brilo, kruda grena surfaco.
Pretiga teknologio: polurado kaj temperado ruliĝanta por 2D aŭ 2B kun 100 ~ 120 abrazivaj materialoj (JIS R6002).
No.4 -- Bona brilo, fajnaj linioj sur la surfaco.
Pretiga procezo: polurado kaj temperado ruliĝanta por 2D aŭ 2B kun 150 ~ 180 abrazivaj materialoj (JIS R6002).
HL -- Arĝentgrizo kun harstrioj.
Pretiga teknologio: 2D-produktoj aŭ 2B-produktoj kun taŭga granulareco de abrazivaj materialoj por polurado de la surfaco estas kontinua abrasiva greno.
SPEGULO -- Spekula.
Pretiga teknologio: 2D-produktoj aŭ 2B-produktoj kun taŭga granulareco de la muelanta materialo muelanta kaj poluranta al la spegula efiko.