316/316L/316Ti Neoksidebla ŝtalo Bobeno
Priskribo
| Tajpu | Grado | Grado | Kemia Komponanto % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Alia | |||
| Aŭstenita | 201 | SUS201 | ≤0,15 | 16.00-18.00 | 3.50-5.50 | 5.50–7.50 | ≤0,060 | ≤0,030 | - | ≤1.00 | - | ≤0,25 | - |
| 202 | SUS202 | ≤0,15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0,060 | ≤0,030 | ≤1.00 | - | ≤0,25 | － | ||
| 301 | 1.431 | ≤0,15 | 16.00-18.00 | 6.00-8.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | ≤0,10 | - | |
| 304 | 1.4301 | ≤0,07 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 304L | 1.4307 | ≤0,030 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 304H | 1.4948 | 0.04-0.10 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 309 | 1.4828 | ≤0,20 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 309S | * | ≤0,08 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 310 | 1.4842 | ≤0,25 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 310S | * | ≤0,08 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 314 | 1.4841 | ≤0,25 | 23.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1.4401 | ≤0,08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316L | 1.4404 | ≤0,030 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316Ti | 1.4571 | ≤0,08 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | 0.1 | Ti5(C+N)~0.70 | |
| 317 | * | ≤0,08 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 317L | 1.4438 | ≤0,03 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 321 | 1.4541 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Ti5(C+N)~0.70 | |
| 321H | * | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Ti5(C+N)~0.70 | |
| 347 | 1.455 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Nb≥10*C% -1.10 | |
| 347H | 1.494 | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Nb≥10*C% -1.10 | |
| xm-19 | Nitronic50 | ≤0,06 | 20.50-23.50 | 11.50-13.50 | 4.0-6.0 | ≤0,045 | ≤0,030 | 1.50-3.00 | ≤1.00 | - | 0,2-0,4 | Nb:0,10-0,30 V:0,10-0,30 | |
| 904L | N08904 | ≤0,02 | 19.0-23.0 | 23.0-28.0 | 4.0-5.0 | ≤0,045 | ≤0,035 | ≤1.00 | 0.1 | Cu:1.0-2.0 | |||
| Dupleksa | 2205 | S32205 | ≤0,03 | 22.0-23.0 | 4,5-6,5 | ≤2.00 | ≤0,030 | ≤0,020 | 3.0-3.5 | ≤1.00 | - | 0.14-0.20 | |
| 2507 | S32750 | ≤0,03 | 24.0-26.0 | 6.0-8.0 | ≤1,20 | ≤0,035 | ≤0,020 | 3.0-5.0 | ≤0,80 | 0.5 | 0.24-0.32 | ||
| * | S32760 | ≤0,03 | 24.0-26.0 | 6.0-8.0 | ≤1.00 | ≤0,030 | ≤0,010 | 3.0-4.0 | ≤1.00 | 0,5-1,00 | 0,2-0,3 | ||
| 2304 | S32304 | ≤0,03 | 21.5-24.5 | 3.0-5.5 | ≤2,50 | ≤0,040 | ≤0,030 | 0,05-0,6 | ≤1.00 | 0,05-0,6 | 0,05-0,2 | ||
| 329 | 1.446 | ≤0,08 | 23.00-28.00 | 2.00-5.00 | ≤1.00 | ≤0,040 | ≤0,030 | 1.00-2.00 | ≤0,75 | - | - | ||
| Ferito | 409 | S40900 | ≤0,03 | 10.50-11.70 | 0.5 | ≤1.00 | ≤0,040 | ≤0,020 | - | ≤1.00 | - | ≤0,030 | Ti6(C+N)~0,50 Nb:0,17 |
| 430 | 1Cr17 | ≤0,12 | 16.00-18.00 | - | ≤1.0 | ≤0,040 | ≤0,030 | - | ≤1.0 | - | - | - | |
| 444 | S44400 | ≤0,025 | 17.50-19.50 | 1 | ≤1.00 | ≤0,040 | ≤0,030 | 1,75-2,5 | ≤1.00 | - | 0,035 | Ti+Nb:0.2+4(C+N)~0.80 | |
| 446 | S44600 | ≤0,20 | 23.00-27.00 | 0,75 | ≤1.5 | ≤0,040 | ≤0,030 | 1.50-2.50 | ≤1.00 | - | ≤0,25 | - | |
| Martensito | 410 | 1Cr13 | 0.08-0.15 | 11.50-13.50 | 0,75 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - |
| 410S | * | ≤0,080 | 11.50-13.50 | 0.6 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 416 | Y1Cr13 | ≤0,15 | 12.00-14.00 | 3) | ≤1,25 | ≤0,060 | ≥0,15 | - | ≤1.00 | - | - | - | |
| 420 | 2Cr13 | ≥0,15 | 12.00-14.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 420J2 | 3Cr13 | 0,26-0,35 | 12.00-14.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 431 | 1Cr17Ni2 | ≤0,20 | 15.00-17.00 | 1.50-2.50 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤0,80 | - | - | - | |
| 440C | 11Cr17 | 0,95-1,20 | 16.00-18.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | 0,75 | ≤1.00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0,07 | 15.00-17.50 | 3.00-5.00 | ≤1.00 | ≤0,035 | ≤0,030 | - | ≤1.00 | 3.00-5.00 | - | Nb 0,15-0,45 |
| 631 | 17-7PH | ≤0,09 | 16.00-18.00 | 6.50-7.50 | ≤1.00 | ≤0,035 | ≤0,030 | - | ≤1.00 | ≤0,50 | - | Al 0,75-1,50 | |
| 632 | 15-5PH | ≤0,09 | 14.00-16.00 | 3.50-5.50 | ≤1.00 | ≤0,040 | ≤0,030 | 2.00-3.00 | ≤1.00 | 2,5-4,5 | - | Al 0,75-1,50 | |
Neoksidebla Ŝtalo Lado Plato Grado Baogu Provizo
| Surfaca finaĵo | Karakterizaĵoj kaj apliko |
| 2B | La surfaca brilo kaj plateco de no 2B estas pli bonaj ol no2D.tiam per speciala surfaca traktado por plibonigi ĝiajn mekanikajn proprietojn, No2B preskaŭ povus kontentigi ampleksajn uzojn. |
| No.1 | Polurita per abrazia zono de grit#100-#200, havas pli bonan brilon kun malkontinua kruda strio, uzata kiel internaj kaj eksteraj ornamaĵoj por konstruaĵo, elektraj aparatoj kaj kuirejaj iloj ktp. |
| Ne.4 | Poluritaj per abraziva zono el grit #150-#180, havas pli bonan brilon kun malkontinua kruda strio, sed pli maldika ol No3, estas uzataj kiel banujo-konstruaĵoj internaj kaj eksteraj ornamaĵoj elektraj aparatoj kuirejaj iloj kaj nutraĵprilaboraj ekipaĵoj ktp. |
| HL | Polurita per abrasiva zono de grit #150-#320 sur la NO.4 finpoluro kaj havas kontinuajn striojn, ĉefe uzataj kiel konstruaĵoj ornamaĵoj liftoj, pordo de konstruaĵo, fronta plato ktp. |
| BA | Malvarme ruliĝita, hele recozita kaj haŭt-pasita, la produkto havas bonegan brilecon kaj bonan refleksivecon kiel spegulo, kuireja aparato, ornamaĵo ktp. |
| 8K | La produkto havas bonegan brilon kaj preferas refleksivecon esti la spegulo. |